Materiales compuestos con base en matrices poliméricas biodegradables para uso en reparación y regeneración de tejido óseo

Gaona Corral, Luis Andrés (2013) Materiales compuestos con base en matrices poliméricas biodegradables para uso en reparación y regeneración de tejido óseo. Doctorado thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

8MB

Resumen

Se pretende aprovechar las propiedades mecánicas y osteogénicas de la Poli (-Caprolactona) (PCL), aumentando su degradabilidad al incorporar un agente hidrofílico como el Poli (Óxido de Etileno) (PEO), o de alta degradabilidad como el Poli (L-Ácido Láctico) (PLLA). Así, poliuretanos a partir de dioles de PCL y PEO como segmentos poliméricos, y Hexametilendiisocianato (HMDI) como agente enlazante, son sintetizados y caracterizados en bajo y alto peso molecular. Los poliuretanos de bajo peso molecular resultan ser altamente cristalinos y presentando dos fases amorfas independientes, pero resultan no tener capacidad de adhesión osteoblástica por el alto contenido de PEO. Para compensar la falta de osteoconductividad, los poliuretanos de alto peso molecular son también sintetizados con menor contenido de PEO, y se evalúan integrando Fibronectina (FN) en la matriz polimérica y Risedronato de Sodio (RSD) en partículas de Hidroxiapatita (HAp), obteniendo materiales compuestos que permiten la proliferación y diferenciación osteoblástica. Se evalúa además la degradación hidrolítica de membranas fabricadas previamente mediante freeze extraction; estas membranas son mezclas de PLLA y PCL, hallando que la relación PLLA/PCL=80/20 w/w se mantiene durante 66 semanas de degradación, a pesar de los cambios en sus propiedades mecánicas y aumento del grado de cristalinidad., Abstract. The objective of this thesis is to take advantage of Poly (-Caprolactone) (PCL) mechanical and osteogenic properties by raising its degradability. It may be achieved by integrating both Poly (Ethylene Oxide) (PEO) as hydrophilic factor, and Poly (L-Lactic Acid) (PLLA) as high degradability agent. So, polyurethanes were synthesized from diols of PCL and PEO as polymeric segments, and Hexamethylene Diisocyanate (HMDI) as bonding agent, yielding low and high molecular weight copolymers, and then characterized. Low molecular weight polyurethanes have high crystal content and show two different amorphous zones, but they have no capability of osteoblastic adhesion because of the high PEO content. In order to improve the osteoconductivity, high molecular weight polyurethanes were also synthesized and characterized using lower PEO content, and then evaluated by incorporating both Fibronectin (FN) in the polymeric matrix and Sodium Risedronate (RSD) in Hydroxyapatite (Hap) particles; indeed, these composites allow osteoblasts to proliferate and differentiate. It was also evaluated the hydrolytic degradation of membranes, which were previously made by freeze extraction technique; these membranes are blends of PLLA and PCL, and it was found that composition PLLA/PCL=80/20 w/w remained during 66 weeks of degradation, besides the changes of its mechanical properties and degree of crystallinity.

Tipo de documento:Tesis/trabajos de grado - Thesis (Doctorado)
Colaborador / Asesor:Perilla Perilla, Jairo Ernesto and Gómez Ribelles, José Luis and Lebourg, Myriam Madeleine
Información adicional:Doctor en Ingeniería - Ciencia y Tecnología de Materiales. Línea de Investigación: Materiales Poliméricos
Palabras clave:Poli (-Caprolactona), Poli (Óxido de Etileno, Osteoblastos, Risedronato de Sodio, Degradación Hidrolítica, Poli (Ácido L-Láctico), Polyurethanes, Poly (-Caprolactone), Poly (Ethylene Oxide), Osteoblasts, Sodium Risedronate, Hydrolytic Degradation, Poly (L-Lactic Acid)
Temática:5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
6 Tecnología (ciencias aplicadas) / Technology > 61 Ciencias médicas; Medicina / Medicine & health
6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecánica
Sede Medellín > Facultad de Minas > Escuela de Mecatrónica > Ingeniería Mecánica
Código ID:11393
Enviado por : Universidad Nacional de Colombia Biblioteca Digital -2-Sede Bogotá
Enviado el día :12 May 2014 13:09
Ultima modificación:12 May 2014 13:09
Ultima modificación:12 May 2014 13:09
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox