Oxidación selectiva de ciclohexeno sobre catalizadores de metales de transición soportados sobre haloisita

Urruchurto Madera, Carlos Mario (2014) Oxidación selectiva de ciclohexeno sobre catalizadores de metales de transición soportados sobre haloisita. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

3MB

Resumen

Se sintetizaron catalizadores de óxidos de cobalto y/o cobre soportados sobre un mineral de arcilla tipo haloisita, por el método de impregnación húmeda, con cargas de 1, 5, 10 y 20 % en peso y una relación molar de 1:1 en todos los sistemas mixtos. Los catalizadores fueron caracterizados por análisis químico elemental utilizando fluorescencia de rayos X, estructuralmente por difracción de rayos X, morfológicamente por microscopía electrónica de transmisión. Se caracterizó la reducibilidad por TPR-H2 y la textura por sortometría de nitrógeno, además se caracterizaron por espectroscopía Raman. Se observó que la morfología nanotubular del soporte no se ve afectada por el proceso de síntesis y se verificó el tipo de especies u óxidos de Co y/o Cu presentes en los catalizadores finales. Todos los sólidos fueron ensayados en la reacción de oxidación selectiva de ciclohexeno, con el propósito de obtener ciclohexenol y ciclohexenona, encontrándose que el mejor catalizador de la serie sintetizada es el de Co-Cu/H (20%) y confirmándose que existe un efecto cooperativo entre estos dos metales; además, se realizaron ensayos adicionales con diferentes condiciones (solvente, soporte, etc.) que permitieron determinar el efecto de dichas condiciones en la reacción., Abstract. Cobalt and/or copper oxide catalysts supported on a clay mineral (halloysite) were synthesized by wet impregnation, using loads of 1, 5, 10 and 20 wt% and a molar ratio of 1:1 in all the mixed systems. The catalysts were characterized by elemental chemical analysis using X-ray fluorescence, structurally by X-ray diffraction, and morphologically by electron microscopy (TEM). The reducibility of species was carried out by TPR-H2 and the texture was studied by N2-adsortion. It was observed that the nanotubular morphology of support was not affected throughout the synthesis process; also the (oxides) species of Co and/or Cu present in the final catalysts were verified. All the solids were tested in the selective oxidation reaction of cyclohexene, in order to obtain ciclohexenol and cyclohexenone. The experiments show that the best catalyst from the synthesized series was that named Co-Cu/H (20%), confirming a cooperative effect between these two metals. Furthermore, several experiments were performed with different conditions (solvent, support etc.) to determine the effect of these conditions on the reaction.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Carriazo Baños, José Gregorio
Información adicional:Magister en Ciencias-Química.
Palabras clave:Oxidación selectiva de ciclohexeno, Haloisita, Óxido de Cobalto Cobre, Óxido de Cobre, Mineral de arcilla, Selective oxidation of cyclohexene, Halloysite, Cobalt oxide, Cupper oxide, Clay mineral
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
6 Tecnología (ciencias aplicadas) / Technology > 66 Ingeniería química y Tecnologías relacionadas/ Chemical engineering
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Química
Código ID:12888
Enviado por : Universidad Nacional de Colombia Biblioteca Digital -3- Sede Bogotá
Enviado el día :17 Junio 2014 16:07
Ultima modificación:17 Junio 2014 16:07
Ultima modificación:17 Junio 2014 16:07
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox