Recubrimientos duros en multicapas de cr/crn obtenidas por sputtering con magnetrón desbalanceado (ubm) y diferentes grados de desbalance

Piratoba, Ulises (2011) Recubrimientos duros en multicapas de cr/crn obtenidas por sputtering con magnetrón desbalanceado (ubm) y diferentes grados de desbalance. MOMENTO - Revista de Física; núm. 43 (2011); 33-43 0121-4470 .

Texto completo

[img]
Vista previa
PDF
18MB

URL oficial: http://revistas.unal.edu.co/index.php/momento/arti...

Resumen

Como recubrimientos duros y tenaces con aplicaciones tribológicas y anticorrosivas, se obtuvieron Nano bicapas de Cr/CrN por sputtering reactivo en atmósferas de Ar y Ar+ N2 respectivamente sobre silicio y sobre acero H13 al cual se le hizo un tratamiento previo de temple y revenido. Se usaron flujos de Ar y N2 de 9 y 3 sccm respectivamente, un magnetrón desbalanceado Gencoa VT 100, que permite variar el coeficiente geométrico de desbalance KG en el rango de 1.37 a 0.87, al variar la posición de su imán central. Se obtuvo una serie de 9 recubrimientos con 3 periodos de bicapa y 3 valores de KG y otra serie de 5 recubrimientos con 5 valores de KG. Todos los recubrimientos se caracterizaron mediante difracción de rayos x (XRD), microscopía electrónica de barrido (SEM) y microscopía de fuerza atómica (AFM) en modo de contacto y contacto intermitente o tapping. Los recubrimientos con espesores entre 1.08 y 1.67 µm, presentaron superficies con formaciones globulares, elipsoidales y piramidales. Con el aumento en el desbalance se incrementaron: la nanodureza, la velocidad de crecimiento de las películas y el tamaño de los granos superficiales. La composición porcentual de las fases Cr, CrN y Cr2N, y las intensidades en los planos de difracción, no mostraron una tendencia definida con el aumento del desbalance., Hard and tough coatings in the form of Cr/CrN bilayers were produced by reactive magnetron sputtering in Ar and Ar+N2 atmospheres respectively onto Si and Steel (H13) substrates. An unbalanced magnetron (GENCOA VT 100) and different Ar and N2 fluxes of 9 and 3 sccm respectively were used. The unbalanced geometric coefficient (KG) was varied between 1.37 and 0.87 by varying the magnetron position. Two series of coatings were produced. The first one of nine samples produced with three different bilayers periods and three different KG values and the second one with five samples produced with five different KG values. All coatings were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (ATM). The coatings with thickness between 1.08 and 1.67 mm showed different surfaces with globular, ellipsoidal and piramidal formation. By increasing the unbalance increased the nano hardness, the growth rate and the particles size. However, the chemical composition and the diffraction planes did not show a definite tendency as a function of unbalance grade.

Tipo de documento:Artículo - Article
Palabras clave:Recubrimientos duros, Multicapas de Cr/CrN, Magnetrón desbalanceado., Hard coatings, multilayers of Cr/CrN, unbalanced magnetrón (UBM).
Unidad administrativa:Revistas electrónicas UN > MOMENTO - Revista de Física
Código ID:34665
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :01 Julio 2014 16:07
Ultima modificación:06 Junio 2018 10:51
Ultima modificación:06 Junio 2018 10:51
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox