Estudio de la hemocompatibilidad de películas de CNx producidas por arco pulsado

Galeano Osorio, Diana Shirley (2010) Estudio de la hemocompatibilidad de películas de CNx producidas por arco pulsado. Maestría thesis, Universidad Nacional de Colombia - Sede Manizales.

Texto completo

[img]
Vista previa
PDF - Versión Enviada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB

Resumen

Se depositaron películas de nitruro de carbono (CNx) a través de la técnica de deposición física en fase vapor mediante arco pulsado variando la temperatura del sustrato y se investigó cómo este parámetro afectó la hemocompatibilidad de los recubrimientos. Para obtener criterios de compatibilidad con la sangre se realizaron pruebas in vitro de trombogenicidad, cuyos resultados fueron correlacionados con la microestructura y rugosidad de las películas obtenidas. En la producción de estas películas se varió la temperatura del sustrato, obteniendo recubrimientos a T. ambiente, 100°C, 150°C y 200°C, dejando constantes parámetros como distancia interelectródica, voltaje, presión de trabajo y número de arcos. Técnicas de análisis tales como espectrosocopías infrarroja y Raman visible, revelaron enlaces químicos entre el C y el N presentes en las películas amorfas, con estructuras tendientes a la formación de una estructura grafítica a medida que se incrementaba la temperatura del sustrato. Sin embargo, a una temperatura crítica, 150°C, esta tendencia fue modificada, presentando una película con una estructura más amorfa, siendo ésta la más dura, 2.5±0,7 GPa y menos rugosa, 0,11±0,01 nm. La baja rugosidad y la estructura más amorfa que presentó este recubrimiento favoreció una mayor hemocompatibilidad, demostrándose además que la compatibilidad sanguínea de las películas de nitruro de carbono es afectada por una relación adecuada ID/IG o sp3/sp2 pero no por un contenido absoluto de enlaces sp3 o sp2 / Abstract: Carbon nitride thin films were obtained through plasma assisted physical vapor deposition technique by pulsed arc, varying the substrate temperature and it was investigated how this parameter affected the hemocompatibility of the films. To obtain approaches of blood compatibility, in vitro thrombogenicity tests carried out whose results were correlated with the microestructure and roughness of the films obtained. The substrate temperature was changed in the production of these films, obtaining coatings under different temperatures, room temperature, 100°C, 150°C and 200°C. Variables such interelectrodic distance, voltage, work pressure and number of arches, remained constant. Infrared spectroscopy, visible Raman spectroscopy were used, and they revealed chemical bonding between C and N atoms in the amorphous thin films, moreover graphite-like structures as the substrate temperature was increased. However, out a critical temperature, 150°C, this tendency broke, and the film was more amorphous. The latter coating was the hardest, 2,5±0,7 GPa, and showed the lowest roughness, 0,11±0.01 nm. This last characteristic favored a best hemocompatibility of the film. Also, it was demonstrated that the blood compatibility of carbon nitride films obtained were affected by the ID/IG or sp3/sp2 ratio, not by the absolute sp3 or sp2.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Arango Arango, Pedro José
Palabras clave:Arco pulsado, Sputtering, Materiales Hemocompatibles, Nitruro de Carbono, Crecimiento de Películas de CNx, Revestimientos protectores, Películas delgadas
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Manizales > Facultad de Ciencias Exactas y Naturales > Departamento de Física y Química
Código ID:3520
Enviado por : Biblioteca Digital Universidad Nacional de Colombia - Sede Manizales
Enviado el día :12 May 2011 20:14
Ultima modificación:12 May 2011 20:14
Ultima modificación:12 May 2011 20:14
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox