Influencia de la microestructura en el comportamiento a desgaste abrasivo evaluado bajo norma ASTM G 65 de depósitos de soldadura antidesgaste aplicados sobre sustratos de acero de baja aleación y bajo carbono / Influence of microstructure on the behavior abrasive wear tested under ASTM G 65 weld deposits on substrates used wear low alloy steel and low carbon

Pérez Cepeda, Jaime Andrés (2011) Influencia de la microestructura en el comportamiento a desgaste abrasivo evaluado bajo norma ASTM G 65 de depósitos de soldadura antidesgaste aplicados sobre sustratos de acero de baja aleación y bajo carbono / Influence of microstructure on the behavior abrasive wear tested under ASTM G 65 weld deposits on substrates used wear low alloy steel and low carbon. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

En la reconstrucción de piezas de maquinarias es esencial el poder determinar la mejor opción en cuanto a material depositado por soldadura para recuperación de geometrías perdidas se refiere. El presente trabajo se desarrolló para mejorar las aplicaciones de recubrimientos duros y material de relleno para la reconstrucción de “sprockets”, pero que se pueda extrapolar al uso en industrias de diferente tipo. Se tomaron en cuenta tres (3) factores, material depositado, temperatura de precalentamiento y de sostenimiento y numero de pases depositados, que afectan las características finales de los recubrimientos duros aplicados por soldadura. Los resultados obtenidos de la aplicación del ensayo de desgaste fueron pérdida en peso y en milímetros cúbicos (mm3) del material, lo cual brindó la resistencia al desgaste de cada una de las capas depositadas. Tomando la probeta que más se acercó al promedio obtenido del anterior ensayo, se cortó para caracterizarla microestructuralmente, tomar mediciones de microdureza en zona cercana a la cara de desgaste, analizar la superficie por microscopia SEM, medir la composición química en la capa desgastada, medir el porcentaje de poros en última capa, medir la rugosidad superficial en zona de desgaste y determinar su estructura por difracción de rayos X.Los recubrimientos obtenidos electrodos con altos contenidos de cromo mostraron las mejores propiedades antidesgaste, seguidos de los recubrimientos aplicados con electrodos con contenidos de manganeso del 15% y los recubrimientos aplicados con electrodos de bajo carbono y bajas y medias aleaciones mostraron los resultados más bajos según las condiciones de laboratorio aplicadas. / Abstract. In the reconstruction of parts of machinery is essential to determine the best option in terms of material deposited by welding geometries recovery losses are concerned. This work was developed to enhance applications of hard coatings and fillers for the reconstruction of sprockets, but can be extrapolated for use inindustries of different types. It took into account three (3) factors, the deposited material, preheating temperature and number of passes support and deposits, which affect the final characteristics of hard coatings applied by welding. Results of applying wear test were weight loss in cubic millimeters (mm3) of material, which provided the wear resistance of each of the layers deposited. Taking the test piece which came closest to the average of the previous test to characterize microstructural cut, take measurements of microhardness in area near the face wear surface analysis by SEM microscopy, to measure the chemical composition of the layer worn, measure the percentage of pores in the final layer, surface roughness measuring wear zone and determine its structure by X-ray diffraction. Hardfacing obtained coatings with high chromium contents showed the best anti-wear properties, followed by coatings applied to electrodes with manganese content of 15% and coatings applied to electrodes under low and medium carbon and alloy showed the lowest scores as the applied laboratory conditions.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Espejo Mora M., Edgar
Información adicional:Magister en Ingeniería – Materiales y Procesos.
Palabras clave:Desgaste Abrasivo; ASTM G 65; Recubrimientos Duros; Aceros / Abrasive Wear; ASTM G 65; Hardfacing Coatings; Steels
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecatrónica
Código ID:4312
Enviado por : Universidad Nacional de Colombia Biblioteca Digital - Sede Bogotá
Enviado el día :20 Septiembre 2011 15:26
Ultima modificación:20 Septiembre 2011 15:26
Ultima modificación:20 Septiembre 2011 15:26
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox