Efecto de la impregnación con polímeros sobre las propiedades mecánicas de la Guadua

Reyes Ortiz, Sandra Patricia (2016) Efecto de la impregnación con polímeros sobre las propiedades mecánicas de la Guadua. Doctorado thesis, Universidad Nacional de Colombia - Sede Bogotá.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

7MB

Resumen

La Guadua angustifolia Kunth ha sido aceptada como elemento estructural en las NSR-10. Sin embargo, debido a su biodegradación y baja durabilidad, continúa siendo objeto de estudios que propenden por mejorar sus propiedades. El objetivo principal de esta investigación fue evaluar el efecto que la impregnación dentro de la Guadua angustifolia Kunth macana con copolímeros a partir de estireno (St), metacrilato de metilo (MMA) y acrilato de butilo (BuA), tiene sobre las propiedades mecánicas de compresión y flexión, la absorción de agua y la variación dimensional. Así como, de identificar el papel del acrilato de butilo como agente plastificante en el copolímero. La copolimerización fue analizada a través de dilatometria, viscosimetria, porcentaje de sólidos, DSC, DTG, FTIR y ensayo a compresión. Los resultados indicaron que la impregnación dentro de la Guadua a. puede realizarse usando la mezcla de monómeros St: MMA: BuA en relación 2:2:1, con 1.0% de PBO y 0,5% de dodecilmercaptano, llevados a 55°C por menos de 90 minutos. La concentración de BuA se estableció para alcanzar mínimo una Tg de 60°C. La infiltración al vacío de sustancias fijadoras de tejido, glutaraldehído 2,5% y solución FAA, dentro de pequeñas probetas de Guadua a., no modificaron la dimensión de los vasos de metaxilema, y aumentaron el índice de cristalinidad. Los resultados de los ensayos a compresión y flexión indicaron que el tratamiento térmico, el tratamiento químico y las impregnaciones con polímeros mejoraron las propiedades mecánicas. También se logró la disminución de absorción de agua y reducir la variación dimensional., Abstract. Guadua angustifolia Kunth accepted as a structural element in the NSR-10, but because of its low durability, it continues being studied to improve their properties. Therefore, the main objective of this study was to evaluate the effect of the impregnation within the Guadua angustifolia Kunth macana with copolymers from styrene (St), methyl methacrylate (MMA) and butyl acrylate (BuA), has on mechanical properties of compression and bending, water absorption and the dimensional variation. In addition, to identify the role of butyl acrylate as a plasticizing agent in the copolymer too. The kinetic constants of polymerization, and the polymerization time were obtained by dilatometry, in that the viscosimetric study was conducted through a cone and plate rheometer. The results indicated that the impregnation inside the Guadua a. may be performed using the monomer mixture St: MMA: BuA in relation 2: 2: 1 respectively, adding 1.0% PBO and 0.5% dodecyl mercaptan, carried at 55°C for less than 90 minutes. BuA concentration was set to achieve a Tg of at least 60°C. Vacuum infiltration of substances for tissue fixation, glutaraldehyde 2.5% and FAA solution, within small specimens of Guadua a., did not change the size of the vessels of metaxylem, and increased the crystallinity index. The compressive and flexural strength results, indicated that heat treatment, chemical treatment and impregnation with polymers, improved mechanical properties. Also that the water absorption decreased, and the dimensional variation was reduced.

Tipo de documento:Tesis/trabajos de grado - Thesis (Doctorado)
Colaborador / Asesor:Landinez Tellez, David Arsenio and Boyaca Mendivelso, Luis Alejandro
Información adicional:Doctor en Ingeniería Ciencia y Tecnología de los Materiales. Línea de Investigación: Nuevos Materiales
Palabras clave:Guadua a., Guadua angustifolia, preservación, Impregnación, Copolímeros, ASTM 143, ASTM 1413, Preservation, Impregnation, Copolymers, Butyl Acrylate, ASTM 143-09, ASTM 1413-07
Temática:6 Tecnología (ciencias aplicadas) / Technology > 66 Ingeniería química y Tecnologías relacionadas/ Chemical engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecánica
Sede Medellín > Facultad de Minas > Escuela de Mecatrónica > Ingeniería Mecánica
Código ID:51512
Enviado por : Doctora Sandra Patricia Reyes Ortiz
Enviado el día :18 Apr 2016 18:08
Ultima modificación:18 Apr 2016 18:08
Ultima modificación:18 Apr 2016 18:08
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox