Síntesis y estudio del acoplamiento cristalográfico y estabilidad química en compósitos Sr2HoNbO6 / YBa2Cu3O(7-∂)

Beltrán Rodríguez, Randirley (2015) Síntesis y estudio del acoplamiento cristalográfico y estabilidad química en compósitos Sr2HoNbO6 / YBa2Cu3O(7-∂). Maestría thesis, Universidad Nacional de Colombia - Sede Bogotá.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

9MB

Resumen

La perovskita compleja Sr2HoNbO6 ha sido sintetizada por el método de reacción a estado sólido. El patrón de difracción de rayos X revela que el material Sr2HoNbO6 tiene una estructura cúbica compleja característica de la estructura cristalina cúbica A2B'B''O6 con constante de red a=8.214 Å la cual tiene un acoplamiento razonable (El desajuste de los parámetros de red es del orden del 6%) con el YBa2Cu3O(7-∂). El análisis de espectroscopía de dispersión de energía de rayos X muestra que el Sr2HoNbO6 no contiene trazas de impurezas. La estabilidad química del Sr2HoNbO6 con el superconductor YBa2Cu3O(7-∂) ha sido estudiada por el patrón de difración de rayos X y mediciones de magnetización como función de la temperatura sobre los compósitos Sr2HoNbO6-YBa2Cu3O(7-∂). Los patrones de difracción de rayos X muestran que todos los picos de difracción de rayos X pertenecen ya sea a Sr2HoNbO6 o YBa2Cu3O(7-∂) sin ningún pico extra detectable. Esto implica que los compuestos Sr2HoNbO6 y YBa2Cu3O(7-∂) permanecen como dos fases separadas diferentes en el compósito sin interacción química. La respuesta magnética muestra que la temperatura de transición superconductora del YBa2Cu3O(7-∂) y los compósitos es de 93.5 K. Las caacterísticas del Sr2HoNbO6 lo hace favorable para que pueda usarse como material sustrato para el crecimiento de películas delgadas superconductoras del YBa2Cu3O(7-∂)., Abstract. The complex perovskite oxide Sr2HoNbO6 has been synthesized by solid-state reaction. X-ray diffraction pattern reveal that Sr2HoNbO6 material has an ordered complex cubic structure characteristic of A2B'B''O6 cubic crystalline structure with lattice constant a=8.214 Å, which has a fairly good lattice matching (lattice mismatch of the order of 6%) with YBa2Cu3O(7-∂). Energy dispersive X-ray analysis shows that Sr2HoNbO6 is free of impurity traces. The chemical stability of Sr2HoNbO6 with YBa2Cu3O(7-∂) superconducting has been studied by X-ray diffraction and measurements of magnetization as a function of temperature on Sr2HoNbO6-YBa2Cu3O(7-∂) composites. X-ray diffraction patterns of the composite shown that all the X-ray diffraction peaks could be indexed for either Sr2HoNbO6 or YBa2Cu3O(7-∂) with no extra peak detectable. This result implies that YBa2Cu3O(7-∂) and Sr2HoNbO6 compounds remain as two different separate phases in the composite with no chemical interaction. Magnetic response shows that superconducting transition temperature of pure YBa2Cu3O(7-∂) and Sr2HoNbO6-YBa2Cu3O(7-∂) composites is 93.5 K. These favourable characteristics of Sr2HoNbO6 show that it can be used as a potential substrate material for growth of YBa2Cu3O(7-∂) superconducting films.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Roa Rojas, Jairo
Información adicional:Maestría en Ciencias Física. LÍnea de Investigación: Superconductividad
Palabras clave:Materiales superconductores, perovskitas dobles, sustratos, Superconducting materials, Double perovskites, Substrates
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Física
Código ID:52325
Enviado por : Randirley Beltrán Rodríguez
Enviado el día :01 Junio 2016 14:35
Ultima modificación:01 Junio 2016 14:35
Ultima modificación:01 Junio 2016 14:35
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox