Propiedades Termoeléctricas de compuestos CaSrCoO

Gallo Manrique, Natalia Lina (2011) Propiedades Termoeléctricas de compuestos CaSrCoO. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

997kB
[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

5MB

Resumen

Utilizando el método de reacción sólida se prepararon muestras policristalinas de Ca3−xSrxCo4O9+d (CaSrCoO) con 0 ≤ x ≤0.15, las cuales presentan una estructura cristalina de carácter ortorrómbico, cuyos parámetros de red aumentaron a medida que se incrementó el contenido de estroncio. Sus propiedades de transporte se estudiaron en el rango de temperatura entre 100 y 290 K a partir de mediciones de coeficiente Seebeck S(T) y resistividad eléctrica r(T) en función de la temperatura y el contenido de Sr. El coeficiente Seebeck es positivo en todo el rango de temperatura estudiado, indicando una conducción a través de portadores de carga positivos, su magnitud decrece con el contenido de Sr, mostrando un comportamiento aproximadamente independiente con la temperatura. La conductividad eléctrica presentó un aumento con el nivel de estroncio siendo máxima para la muestra dopada con una concentración de 0.05, para la cual se reportaron valores cercanos a 520 Scm−1, este comportamiento puede estar relacionado con una disminución en la energía de activación, un aumento en la distancia del hopping ó con alteraciones en la concentración de portadores de carga. A partir de las medidas de S(T) y r(T) se calculó el factor de potencia termoeléctrico PF, el cual alcanza valores máximos cercanos a 45 μW/K2cm en el rango de temperatura entre 130K y 200K, para la muestra con una sustitución de estroncio igual a 0.05. Estos valores permiten considerar este tipo de cerámicas como materiales útiles para el desarrollo de dispositivos termoeléctricos. / Abstract. We have used the solid state reaction method to prepare Ca3−xSrxCo4O9+d polycrystalline samples (0 ≤ x ≤ 0.15), the obtained compounds have an orthorhombic crystalline structure, where the lattice parameters increases with the Sr content. Their transport properties were studied from Seebeck coefficient S(T) and electrical resistivity r(T) measurements as a function of the temperature and Sr content, in the temperature range between 100 and 290 K. The Seebeck coefficient is positive over the measured temperature range, wich suggests a conduction given by positive charge carriers, its magnitude decreases with the Sr content being temperature independent. The electrical conductivity exhibits an increment with the Sr level, it reaches maximum values close to 520 Scm−1, this behavior may be related to a decrease in activation energy, an increase in the hopping distance or to changes in the charge carriers concentration. The thermoelectric power factor PF was obtained from measurements of S(T) and r(T), it reaches maximum values close to 45μW/K2cm. These results become these kind of ceramics promising thermoelectric compounds.Escriba aquí la ecuación.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Rodríguez, Julio Evelio
Información adicional:Magister en Ciencias-Física
Palabras clave:Compuestos de CaSrCoO; Termoelectricidad; Propiedades de transporte; Conducción por hopping / CaSrCoO compounds; Thermoelectricity; Transport properties; Hopping conduction
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Física
Código ID:5274
Enviado por : Universidad Nacional de Colombia Biblioteca Digital - Sede Bogotá
Enviado el día :23 Noviembre 2011 16:32
Ultima modificación:23 Noviembre 2011 16:32
Ultima modificación:23 Noviembre 2011 16:32
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox