Estudio de la evolución de daño de un acero de alta resistencia aplicable a la industria minera.

Avila Balaguera, Kimberly (2016) Estudio de la evolución de daño de un acero de alta resistencia aplicable a la industria minera. Maestría thesis, Universidad Nacional de Colombia-Sede Bogotá.

Texto completo

[img] PDF (Versión final) - Versión Aceptada
Restricted to Sólo usuarios registrados
Available under License Creative Commons Attribution Non-commercial No Derivatives.

11MB

Resumen

A medida que ha avanzado la industria, se han desarrollado nuevos materiales que toman el lugar de otros que ofrecen menor resistencia. Un claro ejemplo de aplicaciones para materiales más resistentes se encuentra en la industria minera, petrolera y automotriz; ya que por su alta demanda y necesidad de constante producción, buscan prolongar los tiempos entre paradas de mantenimiento. A pesar de las mejoras en cuanto a propiedades mecánicas de materiales como aceros, hay factores como las grietas causadas por fatiga mecánica, las cuales, a pesar de que se hagan óptimos seguimientos, pueden aparecer de forma inesperada despertando el interés en entender el comportamiento de origen y propagación y como se ven modificados de acuerdo a procedimientos de conformado. Este trabajo presenta la caracterización microestructural y mecánica del acero estructural S690QL en estado de entrega de fábrica y el tratamiento térmico que aproximó la microestructura desarrollada en la zona afectada térmica en un proceso de corte térmico y/o de soldadura. La caracterización se llevó a cabo empleando ensayo de tracción, tenacidad a impacto Charpy y tenacidad a fractura; siendo este último el mayor énfasis del documento ya que se emplea una probeta SENB para evaluar la propagación de grieta por fatiga para obtener las constantes de la ley de Paris. El documento finaliza con el análisis fractográfico de los dos estados empleando microscopía óptica y microscopía electrónica de barrido (SEM por sus siglas en inglés). La investigación evidenció la disminución de la tenacidad del material afectado térmicamente lo que además redujo el tiempo de propagación de grietas por fatiga; adicionalmente se evidenciaron características de isotropía en el material., Abstract. As the industry has progressed and it have been developed, new materials take the place of others that offer less resistance, a clear example of stronger materials applications are mining, oil and automotive industry; which for its high demand and need for constant production seek to prolong the time between maintenance shutdowns, however, other factors may appear unexpectedly such as cracks caused by fatigue, which It involves trying to understand the behavior of spread and how it is modified according to forming processes. This work presents the microstructural and mechanical characterization of structural steel delivery status S690QL in factory and heat treatment that approached the microstructure developed in the heat affected zone on a process of thermal cutting and welding, using optical and scanning electron microscopy, tensile test, impact and fracture toughness; the latter being the main emphasis of the document and a SENB probe is used to evaluate the fatigue crack propagation constants for the Paris law. The paper concludes with fractographic analysis of the two states. The investigation showed the decrease in toughness of the heat affected materials which also reduced the time propagation of fatigue cracks; characteristics of isotropy is further evidenced in the material.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Rodríguez Baracaldo, Rodolfo
Información adicional:Magister en Materiales y Procesos. Línea de Investigación: Ingeniería de Materiales y Procesos de Manufactura
Palabras clave:Aceros de alta resistencia estructural, Tenacidad a la fractura, Tratamiento Térmico, Integral J, Propagación de Grietas, Ley de Paris, Mecanismos de Fractura, Fatiga, High strength Steel, Heat treatment, Toughness fracture, J-Integral, Crack propagation, Paris law, Fatigue, Fracture Mechanisms
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
6 Tecnología (ciencias aplicadas) / Technology > 68 Manufactura para usos específicos / Manufacture for specific uses
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecatrónica
Código ID:53022
Enviado por : Kimberly Avila Balaguera
Enviado el día :24 Junio 2016 16:30
Ultima modificación:24 Junio 2016 16:30
Ultima modificación:24 Junio 2016 16:30
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox