Fabricación y caracterización de capas delgadas a partir de hilos metálicos nanométricos

Vega Verdugo, Marisol (2016) Fabricación y caracterización de capas delgadas a partir de hilos metálicos nanométricos. Maestría thesis, Universidad Nacional de Colombia - Sede Bogotá.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

16MB

Resumen

En esta tesis se presenta la fabricación y caracterización de películas delgadas a partir de nanohilos de plata usando el método spin coating, con el propósito de analizar las propiedades morfológicas, ópticas y eléctricas de dichas capas y compararlas con las del ITO que es actualmente el material más usado como electrodo transparente en la construcción de diversos dispositivos opto-electrónicos, pero debido a la gran demanda de dichos dispositivos y a la escasez del Indio, se está buscando un posible reemplazo. Se realiza además, un estudio de dos métodos de soldadura de los nanohilos de dichas capas con la finalidad de mejorar la conductividad de las películas de nanohilos de plata sin afectar el valor de la trasmitancia, obteniendo como mejores resultados una disminución en la resistencia de hoja de 4.3 ± 1.4 Ω/□ con el método de soldadura por tratamiento térmico y de 12.9 ± 2.4 Ω/□ con el método de soldadura a partir de presiones , de tal manera que las películas delgadas de nanohilos de plata se consolidan como un buen candidato para reemplazar al ITO como electrodos transparentes en la construcción de dispositivos opto-electrónicos., This thesis presents the fabrication and characterization of thin films from silver nanowires of using the spin coating method by means of the solgel technique, in order to analyze their morphological, electrical and optical properties and compare them with those of ITO (indium and tin) which is currently the most common material used as a transparent electrode in the fabrication of various optoelectronic devices, but due to the high demand for such devices and the shortage of Indio in the world, which tends to run out and abruptly raise its price. Due to these reasons, scientifics are looking for a possible replacement and are precisely the silver nanowire films a promising candidate for this goal. The morphological properties of the deposited films were characterized by scanning electron microscopy (SEM), the electrical properties were determined from the measured values of sheet resistance (Rs) and the optical properties by transmitance. They were studied two methods for welding the nanowires of deposited layers in order to improve the conductivity of the films without affecting the value of the transmittance: subjecting them to heat treatment processes and the application of pressure. By heat treatment it was obtained a decrease in sheet resistance of (4.3 ± 1.4 ) Ω/□ , and by appliying pressure, a decrease of (12.9 ± 2.4) Ω/□, , so that thin films of silver nanowires are consolidated as a good candidate to replace ITO as transparent electrodes in the fabrication of optoelectronic devices.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Ardila Vargas, Angel Miguel
Información adicional:Magíster en Ciencias Fí��sica. Línea de investigaci�ón: Semiconductores Org�ánicos
Palabras clave:Pel��íulas, Nanohilos, Spin coating, Transmitancia, Conductividad, Resistencia de hoja, Soldadura, Films, Nanowires, Spin coating, Transmittance, Conductivity, Sheet resistance, Welding
Temática:5 Ciencias naturales y matemáticas / Science
5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Física > Física
Código ID:54854
Enviado por : Marisol Vega Verdugo
Enviado el día :19 Dec 2016 14:10
Ultima modificación:19 Dec 2016 14:10
Ultima modificación:19 Dec 2016 14:10
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox