Evaluación in Vitro de zirconia Y-TZP sometida a diferentes tratamientos mecánicos después del sinterizado

Gómez Salazar, Blas Carlos Andrés (2016) Evaluación in Vitro de zirconia Y-TZP sometida a diferentes tratamientos mecánicos después del sinterizado. Maestría thesis, Universidad Nacional de Colombia-Sede Bogotá.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

6MB

Resumen

La zirconia Y-TZP de uso odontológico, es un material ampliamente usado para restauraciones individuales y múltiples en rehabilitación, que en la práctica clínica debe ser rectificado por el protesista de forma manual, mediante fresas diamantadas a alta velocidad y microarenado con particulado cerámico a diferentes tamaños y presiones para optimizar la adaptación de las estructuras, por un lado, y aumentar la rugosidad superficial, para mejorar la adhesión, por el otro. Estos procedimientos alteran la superficie del material generando grietas de hasta 15µm de profundidad, produciendo esfuerzos residuales y alterando su fase química, lo que se traduce en un descenso en la resistencia a la flexión y por consiguiente un descenso en su confiabilidad clínica. El objetivo de este estudio fue evaluar las características morfológicas, esfuerzos residuales y resistencia a la flexión in Vitro de la zirconia Y-TZP de uso odontológico sometido a diferentes tratamientos de superficie después de sinterizado y un protocolo de regeneración mecánica, haciendo un seguimiento a su comportamiento en el tiempo, mediante 5 grupos (n=15) así: Microarenado con Al2O3 con fines de mejoramiento de la cementación con y sin Microgranallado con fines de regeneración; rectificación con puntas diamantadas de 25- 40µm con y sin Microgranallado con fines de regeneración; y un control sin tratamiento pos-sinterización. Se realizó análisis SEM (caracterización del daño), DRX (medición de esfuerzos residuales) y pruebas de resistencia a la flexión en máquina universal de ensayos, al inicio del estudio y en dos momentos más en el tiempo, después de realizado el tratamiento mecánico y/o tratamiento de regeneración (60 y 120 días). Los grupos de microgranallado y microarenado presentaron un aumento significativo de la resistencia a la flexión p=0.0082 con relación al grupo de fresado. Las mediciones mediante DRX no mostraron significancia el tiempo en las probetas tratadas mecánicamente, ni se relacionan con los valores de resistencia a la flexión., Abstract. The Y-TZP zirconia for dental use, is a material widely used for individual and multiple restorations in prosthodontics, which in clinical practice must be manually rectified by the clinician, using high-speed diamond drills and micro sandblasting with ceramic particulate at different sizes and pressures to optimize the adaptation of the structures on the one hand and increase surface roughness to improve adhesion on the other. These procedures alter the material surface generating cracks up to 15μm deep, producing residual stresses and altering it chemical phase, which results in a decrease in flexural strength and consequently a decrease in clinical reliability. The aim of this study was to evaluate the morphological characteristics, residual stresses and flexural strength of in Vitro dental use zirconia YTZP subjected to different surface treatments after sintering and a protocol of mechanical regeneration, monitoring their behavior by the time, by means of 5 groups (n = 15) as follows: Micro sandblasting with Al2O3 for improvement of the cementation with and without Micro shot peening for regeneration purposes; Rectification with diamond tips 25-40μm with and without micro shot peening for regeneration purposes; And a control without postsintering treatment. SEM (damage characterization), XRD (measurement of residual stresses) and flexural strength tests in a universal testing machine were performed, at the beginning of the study and at two moments in time, after the mechanical and / or Regeneration treatment (60 and 120 days). The groups of micro shot peening and micro sandblasting presented a significant increase of the flexural strength p = 0.0082 vs the milling group. The XRD technique is not reliable for making measurements over time whenever the material was machined in the surface, nor is it related to flexural strength measurements.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Cortés Rodríguez, Carlos Julio and Calle Ujueta, Martha Lucía
Información adicional:Magíster en Odontología. Línea de Investigación: Biomateriales.
Palabras clave:Zirconium oxide, Y-TZP ceramics, Phase transformation, Dental Ceramics, Stress analysis/Methods, Surface properties
Temática:5 Ciencias naturales y matemáticas / Science > 51 Matemáticas / Mathematics
5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
6 Tecnología (ciencias aplicadas) / Technology > 61 Ciencias médicas; Medicina / Medicine & health
Unidad administrativa:Sede Bogotá > Facultad de Odontología
Código ID:57867
Enviado por : Universidad Nacional de Colombia Biblioteca Digital - Sede Bogotá
Enviado el día :27 Julio 2017 13:53
Ultima modificación:27 Julio 2017 13:53
Ultima modificación:27 Julio 2017 13:53
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox