Efecto de la temperatura de recocido sobre las propiedades ópticas y estructurales de películas delgadas de GaSb depositadas por DC magnetron sputtering

Sarmiento Cruz, Norma Diana (2018) Efecto de la temperatura de recocido sobre las propiedades ópticas y estructurales de películas delgadas de GaSb depositadas por DC magnetron sputtering. Maestría thesis, Universidad Nacional de Colombia - Sede Bogotá.

Esta es la última versión del ítem.

Texto completo

[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

Conocer las características estructurales y ópticas de determinados semiconductores es un factor importante para la fabricación de dispositivos con el fin de saber sus propiedades y mejorar la eficiencia de los mismos. El semiconductor fabricado y caracterizado en este trabajo, el Antimoniuro de Galio, GaSb, es ampliamente conocido en el campo de los semiconductores por diversas aplicaciones y por tal motivo en este proyecto se depositaron películas delgadas de GaSb a través del método de pulverización catódica, bajo diferentes parámetros de síntesis, entre ellos el tiempo de depósito (5min y 15min) y la temperatura de recocido (de 300°C a 350°C). Para ello a las películas delgadas de les realizaron estudios de Difracción de rayos X (XRD, por sus siglas en inglés) para la identificación de fases y estructura del cristal y se midió igualmente la transmitancia y reflectancia para identificar las contantes ópticas (índice de refracción, Gap óptico y coeficiente de absorción). Se pudo observar que tanto la temperatura de recocido como el tiempo de depósito influyen en las propiedades estudiadas, logrando mejorar la cristalización del material y su capacidad de absorción de la luz bien sea al aumentar la temperatura de recocido y/o el tiempo de depósito., Abstract: Knowing structural and optical features of certain semiconductors is an important factor for devices manufacture, with the aim of learning their properties and improves their efficiency. The Galium Antimonide, GaSb is the semiconductor manufactured and characterized in this thesis, it is widely known in the field of semiconductors for its various applications, therefore in this project, thin films of GaSb were deposited through the method of cathodic sputtering, carried out under different parameters of synthesis, including settle time (5min and 15min) and annealing temperature (from 300° C to 350° C). To this effect, X-ray diffraction (XRD) studies were carried out to the thin films for identifying the stages and structure of the crystal and the transmittance and reflectance were measured to identify the optical counters (refractive index, optical Gap and absorption coefficient). It was observed that both, the annealing temperature and the deposition time influence the properties studied, achieving to improve the material crystallization and its ability to absorb light, either by increasing the annealing temperature and / or the storage time. Keywords: DC magnetron Sputtering, binary Semiconductor, GaSb, optical properties, structural properties

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Dussan Cuenca, Anderson
Información adicional:Magíster en Ciencias - Física. Línea de Investigación: Fabricación de Dispositivos Nanoestructurados con Aplicaciones Tecnológicas.
Palabras clave:DC magnetron Sputtering, Semiconductor binario, GaSb, Propiedades ópticas, Propiedades estructurales, DC magnetron Sputtering, Binary Semiconductor, Optical properties, Structural properties
Temática:5 Ciencias naturales y matemáticas / Science
5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Física
Código ID:64305
Enviado por : Norma Diana Sarmiento
Enviado el día :12 Junio 2018 19:46
Ultima modificación:12 Junio 2018 19:46
Ultima modificación:12 Junio 2018 19:46
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Versiones disponibles de este ítem.

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox