Escudo de la República de Colombia
Sistema Nacional de Biliotecas - Repositorio Institucional Universidad Nacional de Colombia Biblioteca Digital - Repositorio Institucional UN Sistema Nacional de Bibliotecas UN

Lixiviación atmosférica de minerales lateríticos colombianos de bajo tenor de níquel, en medios clorurados

Garces Granda, Adriana del Pilar (2018) Lixiviación atmosférica de minerales lateríticos colombianos de bajo tenor de níquel, en medios clorurados. Doctorado thesis, Universidad Nacional de Colombia Sede Medellin.

Texto completo

[img]
Vista previa
PDF
Available under License Creative Commons Attribution No Derivatives.

12MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

28MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

20MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

En este estudio una laterita colombiana con un contenido de Ni del 1.15%, 0.12% de Co y 41.1% de Fe se utilizó para evaluar el comportamiento cinético de dicha muestra en un proceso de lixiviación atmosférica usando ácido clorhídrico con adición de una sal de cloruro de sodio. Adicionalmente, se planteó la aplicación de una etapa de pretratamiento térmico con el fin de exponer el níquel a la interfaz de reacción. Su extracción, en una etapa subsiguiente de lixiviación, se incrementó de 16% a 98% cuando la muestra se calcinó a 430ºC por 1 horas. De acuerdo a los resultados, el níquel está incorporado uniformemente en los óxidos de hierro y por tal razón, se requiere una disolución completa de las partículas del óxido para lograr una alta extracción de níquel. La concentración de HCl, concentración total de iones cloruro y la temperatura de lixiviación también mostraron tener un efecto directo en la extracción del metal. La disolución de níquel se ajustó a un modelo de núcleo recesivo de control por reacción química, con energías de activación del orden de 103.2 kJ/mol y 97.9 kJ/mol para la muestra sin calcinar y calcinada, respectivamente., Abstract: In this study, a Colombian nickel laterite with 1.15% Ni, 0.12% Co and 41.1% Fe was used to evaluate its kinetic behavior during an atmospheric leaching process using hydrochloric acid with the addition of sodium chloride. Additionally, the application of a thermal pre-treatment step was proposed in order to expose the nickel to the surface reaction. During the leaching stage, nickel extraction was increased from 16% to 98% when the sample was calcined at 430ºC for 1 hour. According to the results, a complete dissolution of the oxide particles is required to achieve a high nickel extraction because the metal is uniformly incorporated in the iron oxides. Hydrochloric acid concentration, total chloride ions concentration and the leaching temperature also showed to have a direct effect on nickel extraction. Nickel dissolution was adjusted to a chemical control shrinking core model with activation energies about to 103.2 kJ/mol and 97.9 kJ/mol for the raw and calcined sample, respectively

Tipo de documento:Tesis/trabajos de grado - Thesis (Doctorado)
Colaborador / Asesor:Restrepo Baena, Oscar Jaime
Información adicional:Línea de Investigación: Metalurgia Extractiva
Palabras clave:Níquel, Lateritas Colombianas, Lixiviación ácida, Lixiviación atmosférica, Calcinación
Temática:5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
5 Ciencias naturales y matemáticas / Science > 55 Ciencias de la tierra / Earth sciences & geology
6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales > Ingeniería de Minas y Metalurgia
Código ID:64439
Enviado por : Adriana del Pilar Garces Granda
Enviado el día :20 Junio 2018 17:34
Ultima modificación:02 Mar 2019 15:23
Ultima modificación:02 Mar 2019 15:23
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem