CARACTERIZACIÓN TEXTURAL Y QUÍMICA DE CARBONES ACTIVADOS PREPARADOS A PARTIR DE CUESCO DE PALMA AFRICANA (ELAEIS GUINEENSIS) POR ACTIVACIÓN QUÍMICA CON CaCl2 y MgCl2

Acevedo, Sergio and Giraldo, Liliana and Moreno, Juan Carlos (2015) CARACTERIZACIÓN TEXTURAL Y QUÍMICA DE CARBONES ACTIVADOS PREPARADOS A PARTIR DE CUESCO DE PALMA AFRICANA (ELAEIS GUINEENSIS) POR ACTIVACIÓN QUÍMICA CON CaCl2 y MgCl2. Revista Colombiana de Química, 44 (3). pp. 18-24. ISSN 2357-3791

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial.

243kB

URL oficial: https://revistas.unal.edu.co/index.php/rcolquim/ar...

Resumen

Se obtuvieron carbones activados mediante activación química de cuesco de palma africana (Elaeis Guineensis) con soluciones de cloruro de magnesio y cloruro de calcio a diferentes concentraciones. Los materiales preparados se caracterizaron textural y químicamente. Los resultados obtenidos muestran que los carbones activados con los mayores valores de área superficial y volumen de poro se obtienen cuando se emplean soluciones con las menores concentraciones del agente activante. Los carbones activados obtenidos presentan áreas superficiales y volúmenes de poro con valores entre 10 y 501 m2/g y 0,01 y 0,29 cm3/g respectivamente. Los valores de las entalpías de inmersión de los sólidos en agua se encuentran entre -14,3 y -32,8 J/gy en benceno entre -13,9 y -38,6 J/g. La acidez y la basicidad total de los carbones activados presentan valores entre 23 y 262 µmol/g y 123 y 1724 µmol/g respectivamente. También se determinó el pH en el punto de carga cero, con valores entre 4,08 y 9,92 para el conjunto de los carbones activados. Los resultados muestran que la activación con las sales MgCl2 y CaCl2 producen carbones activados con poros en el rango de los mesoporos que facilitan la entrada del adsorbato al interior del material., Activated carbons through chemical activation of African palm shells (Elaeis guineensis) with magnesium chloride and calcium chloride solutions at different concentrations were obtained. The prepared materials were characterized textural and chemically. The results show that activated carbons with higher values of surface area and pore volume are obtained when solutions with lower concentrations of the activating agent are used. The obtained activated carbons have surface areas and pore volumes with values between 10 and 501 m2 /g and 0.01 and 0.29 cm3 /g respectively. Immersion enthalpies values of solids in water were between -14.3 and -32.8 J/g and benzene between -13.9 and -38.6 J/g. Total acidity and basicity of the activated carbons had values between 23 and 262 μmol/g 123 and 1724 μmol/g respectively. pH at the point of zero charge was also determined with values between 4.08 and 9.92 for set of activated carbons . The results show that activation with CaCl2 and MgCl2 salts produce activated carbons with pores in the range of mesopores for facilitate entry of the adsorbate into the materials.

Tipo de documento:Artículo - Article
Palabras clave:activated carbon, CaCl2 solution, MgCl2 solution, immersion enthalpy, carbón activado, solución de CaCl2, solución de MgCl2, entalpía de inmersión
Temática:5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
Unidad administrativa:Revistas electrónicas UN > Revista Colombiana de Química
Código ID:67321
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :18 Septiembre 2018 21:19
Ultima modificación:18 Septiembre 2018 21:19
Ultima modificación:18 Septiembre 2018 21:19
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox