CARACTERIZACIÓN MAGNÉTICA E HIPERFINA DE LA TRANSFORMACIÓN TÉRMICA CuO - Fe2O3 A Fe3O4

Betancur, Juan D. and Restrepo, Johans and Fernandez, Jhon J. and Perez, Oswaldo (2018) CARACTERIZACIÓN MAGNÉTICA E HIPERFINA DE LA TRANSFORMACIÓN TÉRMICA CuO - Fe2O3 A Fe3O4. MOMENTO (56). pp. 63-75. ISSN 2500-8013

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution No Derivatives.

1MB

URL oficial: https://revistas.unal.edu.co/index.php/momento/art...

Resumen

Se presenta un estudio magnético acerca de la transformación térmica de hematita dopada con CuO (Fe2O3 + CuO). El tratamiento térmico se realizó a una temperatura de 375 ± 1 ºC, en una atmosfera controlada compuesta por 20% de hidrogeno y 80% de nitrógeno. Las muestras fueron caracterizadas por espectroscopía Mössbauer a temperatura ambiente, magnetización en función de la temperatura y ciclos de histéresis a 10K. Los resultados sugieren que los campos hiperfinos y los anchos de línea A y B permanecen esencialmente constantes con el aumento de la concentración de CuO, mientras que a la vez surge una componente paramagnética, lo cual es indicativo de la aparición de un precipitado o nueva fase de Fe-Cu, i.e. no hay una incorporación efectiva del cobre en la estructura de la magnetita. La magnetización de saturación cae aproximadamente de 87 emu/g a 78 emu/g, consistente con la presencia de dicha fase paramagnética. Se presenta también un aumento de la coerctividad desde ~576 Oe hasta ~621 Oe con el aumento del %CuO desde 2% hasta 20 %. Tal aumento se atribuye también a dicha fase paramagnética actuando como centro de anclaje de las paredes de dominio, sumado al efecto de anclaje de las posibles vacancias inducidas por el tratamiento térmico. Finalmente, se observa una inversión de la magnetización en la temperatura de Verwey. Los datos sugieren que mediante el método de síntesis empleado se obtienen partículas de magnetita Fe3O4 coexistiendo con precipitados de Fe-Cu, lo cual modifica las propiedades magnéticas y genera un efecto interesante en la magnetización a la temperatura de Verwey., A magnetic study about the thermal transformation of hematite doped with CuO (Fe2O3 + CuO) is presented. The heat treatment was carried out at a temperature of 375 ± 1 ºC, in a controlled atmosphere composed by 20% hydrogen and 80% nitrogen. Samples were characterized by Mössbauer spectroscopy at room temperature, magnetization as a function of temperature and hysteresis loops at 10K. Our results suggest that both the hyperfine fields and linewidths of the A and B sites remain essentially constant with increasing the CuO concentration, while at the same time a paramagnetic component arises, which is indicative of the appearance of a precipitate or a new phase of Fe-Cu, i.e. there is not an effective incorporation of the copper into the structure of the magnetite. The saturation magnetization falls from approximately 87 emu/g to 78 emu/g, consistent with such a paramagnetic phase. Also, an increase in the coercivity from ~576 Oe up to ~621 Oe by increasing the percentage of CuO from 2% up to 20% is observed. Such increase is also attributed to the paramagnetic phase acting as pinning center for domain walls, besides also de pinning effect due to vacancies induced by the thermal treatment. Finally, an inversion of the magnetization in the Verwey temperature is observed. The data suggest that by means of the synthesis method employed, it is possible to obtain Fe3O4 magnetite particles coexisting with precipitates of Fe-Cu, giving rise to a modification in the magnetic properties and generatingan interesting effect in the magnetization at the Verwey temperature.

Tipo de documento:Artículo - Article
Palabras clave:Magnetite, Hematite, Mössbauer Spectroscopy, Verwey Temperature, Magnetita, Hematita, Espectroscopia Mössbauer, Temperatura de Verwey
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
5 Ciencias naturales y matemáticas / Science
Unidad administrativa:Revistas electrónicas UN > MOMENTO - Revista de Física
Código ID:68341
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :21 Septiembre 2018 14:02
Ultima modificación:21 Septiembre 2018 14:02
Ultima modificación:21 Septiembre 2018 14:02
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox