DIFUSIVIDAD TÉRMICA DE MONO-CRISTALES DE GaSb Y Si(100)

Pulzara Mora, Alvaro and Bernal Correa, Roberto and Acevedo Rivas, Alvaro and Rosales Rivera, Andrés (2015) DIFUSIVIDAD TÉRMICA DE MONO-CRISTALES DE GaSb Y Si(100). MOMENTO (51). pp. 31-44. ISSN 2500-8013

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution No Derivatives.

6MB

URL oficial: https://revistas.unal.edu.co/index.php/momento/art...

Resumen

En este trabajo, reportamos la caracterización de monocristales de Si(100) y GaSb(111) utilizando espectroscopia Raman y fotoacústica (principal interés) en configuración abierta y cerrada, para compuestos semiconductores III-V con estructura tipo zinc blenda, los espectros Raman generalmente muestran dos picos, un pico a baja frecuencia correspondiente a modos fononicos TO y un pico en alta frecuencia correspondiente a modos fononicos LO. Un fuerte pico es mostrado en la posición 226 cm−1 y uno un poco más débil en 237 cm−1, que son los modos TO y LO respectivamente, debido a la orientación cristalina del material. Con el fin de determinar la difusividad térmica de los materiales se utilizaron láseres con longitudes de onda de 650 nm y 535 nm. Los resultados de la difusividad térmica de los monocristales de Si y GaSb, obtenidos a partir del modelo de Rosencwaig y Gersho (RG) se analizaron en función de la orientación cristalográfica. Discutimos la recombinación no-radiativa que se origina en la superficie y en el volumen del cristal, que contribuye a la señal fotoacústica, en términos del tipo de celda y de la línea de excitación., In this work, we report the characterization of Si (100) and GaSb (111) single crystals by using Raman spectroscopy and a photoacoustic cell in open and closed configuration. For III-V compound semiconductors of the zinc-blende crystal structure, Raman spectra generally show two peaks. The lower-frequency peak corresponds to TO phonons, and the higher frequency peak corresponds to LO phonons. A strong peak was found at 226 cm−1 and a weak peak at 237 cm−1, which are the TO and LO modes, respectively. Raman spectrum of GaSb (111) show that the integrate intensity of TO mode is greater than LO mode due to disoriented of the single crystal. In order to obtain the thermal diffuivity, the crystals were exciting by means of solid-state lasers of wavelengths of 650 nm and 535 nm, respectively. The results of the thermal diffusivity of single crystals, obtained from the Rosencwaig and Gersho (RG) model were analyzed according to the crystallographic orientation. We have also discussed the contribution of the non-radiative recombination to the photoacustic signal from surface and bulk depending on the type of cell and excitation of the laser line.

Tipo de documento:Artículo - Article
Palabras clave:Photoacoustic, Semiconductors, non-radiative recombination., Fotoacústica, Semiconductores, recombinación no radiativa.
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
5 Ciencias naturales y matemáticas / Science
Unidad administrativa:Revistas electrónicas UN > MOMENTO - Revista de Física
Código ID:68403
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :21 Septiembre 2018 14:02
Ultima modificación:21 Septiembre 2018 14:02
Ultima modificación:21 Septiembre 2018 14:02
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox