EFECTO DEL VOLTAJE SOBRE LA FORMACIÓN DE NANOESTRUCTURAS DE TiO2 VÍA ANODIZADO ELECTROQUÍMICO

Quiroz, Heiddy P. and Dussan, Anderson and Quintero, Francisco and Arias, Pedro J. and Zea, Hugo R. (2014) EFECTO DEL VOLTAJE SOBRE LA FORMACIÓN DE NANOESTRUCTURAS DE TiO2 VÍA ANODIZADO ELECTROQUÍMICO. MOMENTO (49). pp. 36-46. ISSN 2500-8013

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution No Derivatives.

1MB

URL oficial: https://revistas.unal.edu.co/index.php/momento/art...

Resumen

En este trabajo se fabricaron arreglos de nanotubos de TiO2 por el método de anodizado electroquímico usando tanto para el ánodo como para el cátodo láminas de Ti y diferentes voltajes deanodización. Para la preparación de las muestras se usó una mezcla de agua y solución de etilenglicol a temperatura ambiente cambiando el tiempo de síntesis durante la reacción. Se realizaron procesos de recocido a todas las muestras en el rango entre 273 y 723 K, sin observarse cambios en las propiedades morfológicas del material. A partir de medidas de difracción de rayos X fueron identificadas las fases rutilo y anatasa en todas las muestras; cuando la temperatura de recocido superó los 723 K, se observó un cambio estructural de la fase anatasa a rutilo. A partir de medidas de SEM se observó que el tamaño del diámetro interno de los nanotubos varió entre 37 nm y 41 nm cuando el voltaje de anodización fue alternante y constante, respectivamente. Se observó que un tamaño de ~6 um de longitud y 29,56 nm de espesor de la barrera del tubo están influenciados por el voltaje de anodización constante de 80 V; sin embargo nanotubos con forma de guadua se evidenciaron cuando se aplicó un voltaje alternantede 80 V y 20 V durante 1 minuto y 5 minutos respectivamente. Sepresenta una correlación entre los parámetros de síntesis y laspropiedades morfológicas., In this work TiO2 nanotubes arrays were obtained by electrochemical anodization method using Ti foil, both anode and cathode, and under different anodization voltages. A mix of water and ethylene glycol as electrolyte was used at environment temperature for several times of reaction. Annealing process to TiO_2 samples were realized at temperature between 273 and 723 K without changes on morphological properties. Rutile and anatase phases were identified by X-ray diffraction measurements in all samples and a change of anatase to rutile phase was observed at biggest annealing temperature (T=723 k). From SEM measurements the inner diameter size for nanotubes were obtained, varying between 37 nm and 41 nm when anodizing voltage was alternant and constant, respectively. Nanotubes with ~6 um of length and 29.56 nm thickness of barrier layer were obtained as influence of the anodizition voltage of 80 V fixed; however nanotubes with bamboo form were observed at alternant voltage of 80 and 20 V during 1 minute and 5 minutes, respectively. A correlation between deposition parameters and morphological properties is presented.

Tipo de documento:Artículo - Article
Palabras clave:TiO2, Titanio, Nanotubos, TiO2, Titanium, Nanotubes
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
5 Ciencias naturales y matemáticas / Science
Unidad administrativa:Revistas electrónicas UN > MOMENTO - Revista de Física
Código ID:68430
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :21 Septiembre 2018 14:03
Ultima modificación:21 Septiembre 2018 14:03
Ultima modificación:21 Septiembre 2018 14:03
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Metabiblioteca OAIster BASE BDCOL Registry of Open Access Repositories SNAAC Red de repositorios latinoamericanos eprints Open archives La referencia Tesis latinoamericanas OpenDOAR CLACSO
Este sitio web se ve mejor en Firefox