Estudio del efecto conjunto de la fluorita y el yeso como mineralizadores en la fabricación de cemento portland I/ Joint efect of the fluorite and the gypsum as mineralizers in the manufacture of Portland cement I

Díaz Burbano, María Fernanda (2012) Estudio del efecto conjunto de la fluorita y el yeso como mineralizadores en la fabricación de cemento portland I/ Joint efect of the fluorite and the gypsum as mineralizers in the manufacture of Portland cement I. Maestría thesis, Universidad Nacional de Colombia, Sede Medellín.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial.

2MB

Resumen

En este trabajo se presenta el estudio del efecto conjunto de los mineralizadores fluorita (CaF2) y yes No (CaSO4.2H2O) para reducir la temperatura de clinkerización para la producción de cemento Portland I. Se empleó el diseño estadístico de experimentos Box-Behnken para evaluar a nivel de laboratorio los efectos sobre la cal libre de la cantidad de fluorita en los porcentajes 0.00%, 0.25%, 0.50% y 0.75%, la relación fluorita/yeso de 2/15, 1/3 y 8/15, y temperatura de clinkerización a 1250°C, 1300°C y 1350°C. Se caracterizó el clinker obtenido y se encontró disminución de la cal libre de un 81% y de un 56% en el clinker mineralizado con una relación fluorita/yeso de 2/15, comparado con el clinker sin mineralizador a 1300°C y 1250°C respectivamente. Mediante análisis petrográfico se evidenció la aparición de silicatos y aluminatos cálcicos a menor temperatura cuando se incorporaron los mineralizadores a las materias primas. La cantidad de alita (C3S) del clinker mineralizado a 1250°C y 1300°C, es mayor al clinker convencional (1450°C). Estos resultados permiten concluir que es posible reducir temperaturas de clinkerización en aproximadamente 150°C y por ende el consumo energético y las emisiones mediante el uso de fluorita y yeso en la producción de clinker, lo cual se traduce además en eficiencia energética, económica y ambiental./Abstract. This work presents a study of the joint effect of fluorite (CaF2) and gypsum (CaSO4.2H2O) as mineralizers on the clinkerization temperature reduction in the manufacture of Portland cement I. A Box-Behnken statistical design of experiment was used at lab scale to understand the effect of fluorite at percentages of 0.00% 0.25%, 0.50% and 0.75%, fluorite/gypsum ratio at 2/15, 1/3 and 8/15, and clinkerization temperature at 1250°C, 1300°C and 1350°C, with free CaO as response variable. The clinker produced was characterized and a decrease of 81% and 56% of free CaO in the clinker with mineralizer with fluorite/gypsum ratio at 2/15 compared to the same clinker without mineralizer at 1300°C and 1250°C respectively was found. Also, a petrographic analysis displayed the appearance of calcium silicates and aluminates at a lower temperature when the mineralizers are incorporated into the raw materials. The amount of alite (C3S) of mineralized clinker at lower temperatures (1350°C, 1300°C) is larger than that of the alite of conventional clinker. These results show that fluorite and gypsum mineralizers are useful to reduce clinkerization temperature by approximately 150°C and therefore the energy consumption and emissions which represent high cost in the cement industry

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor: Restrepo Baena, Oscar Jaime and Tobón, Jorge Iván
Palabras clave: Mineralizadores; Fluorita; Yeso; Clinker; Temperatura; Clinkerización; Mineralizers; Fluorite; Gypsum; Clinker; Temperature; Clinkerization
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales
Código ID:7117
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :27 Julio 2012 22:51
Ultima modificación:27 Julio 2012 22:51
Ultima modificación:27 Julio 2012 22:51
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox